Brief Analysis of the Application of High Temperature Glass Ink

High-temperature glass ink, also known as high-temperature tempered glass ink, has a sintering temperature of 720-850 ° C. After high-temperature tempering, the ink and glass are firmly fused together, and are widely used in building curtain walls, car glass, stove oven panels, etc. The high-temperature glass ink has been baked to 850 degrees (the baking temperature is selected according to product requirements) and the vitreous body is integrated to achieve the glass surface coloring effect. The color of the high-temperature glass ink and the vitreous after high-temperature baking is permanent and very stable. The color of the high-temperature glass ink is bright, the surface of the vitreous body is also very smooth, and it has good light transmittance and high-end temperament.

High temperature glass ink has a wide range of uses, mainly used for high-end glass handicrafts, such as: high-end glass handicrafts, glasses, glass lamps, glass lampshades, glass wine bottles and other glass products that require high added value. High temperature glass ink has a wide range of processing technologies available, which can be used for spraying, printing, roll printing and dripping and hand-painting. High temperature glass ink can also be made into transfer printing paper to print on irregular glass parts. High temperature glass ink can be made into thermoplastic block pigments for hot printing screen.

During the use of the high-temperature glass ink, it should be fully mixed with the toner. It is best to grind it 2-3 times with a three-roll grinder. For spraying and hand-painting, you need to use Tianna water or alcohol to adjust the construction consistency and drying speed to avoid sagging. After the glass workpiece is lustful, it is best to use the high-temperature glass ink to dry it at a temperature of 150-200 degrees Celsius, or to dry it in a dust-free workshop, so that it can be put into the kiln in batches for grilling. The grilling time of the high-temperature glass ink should be controlled at 90-120 minutes. If the time is too short, it will affect the delicacy of the process surface. If the high-temperature glass ink is grilled in a sealed kiln, the vent of the kiln must be opened before the temperature is 400 degrees Celsius. After the organic substances of the oily toner are completely volatilized, the vent must be closed to maintain the atmosphere in the kiln so as not to affect the firing color..

The above is the application of high temperature glass ink. If you want to know more information about congeneric products, you can call Zibo Opal Chemical Materials Co., Ltd., which focuses on the research and development of water-based toner and ceramic glass inkjet ink. The company produces water-based toner, which is green and environmentally friendly, easy to clean with water, and its performance indicators exceed imported congeneric products, which is the first in China.