Discussion on post-press drying process of high temperature glass ink for automobile

In automotive glass screen printing, high-temperature glass ink is mainly used. Before the glass is tempered or thermally bent, the ink printed on the glass surface must be dried, and the drying process of these ink layers has an impact on screen printing. Quality and speed play a crucial role.

2021

12-19

The vigorous development of high temperature glass ink

The vigorous development of screen printing has accelerated the development of various new types of screen printing high-temperature glass inks, such as fragrance, fluorescence, foaming, and quick-drying inks. These inks are generally dried at room temperature, and only glass printing and ceramics are dried at high temperatures. Dry at high temperatures, so high temperature resistant glass inks often refer to inks used for glass and ceramic printing.

2021

12-19

Brief Analysis of the Application of High Temperature Glass Ink

High-temperature glass ink, also known as high-temperature tempered glass ink, has a sintering temperature of 720-850 ° C. After high-temperature tempering, the ink and glass are firmly fused together, and are widely used in building curtain walls, car glass, stove oven panels, etc. The high-temperature glass ink has been baked to 850 degrees (the baking temperature is selected according to product requirements) and the vitreous body is integrated to achieve the glass surface coloring effect. The color of the high-temperature glass ink and the vitreous after high-temperature baking is permanent and very stable. The color of the high-temperature glass ink is bright, the surface of the vitreous body is also very smooth, and it has good light transmittance and high-end temperament.

2021

12-19

Study on Polyurethane Adhesive for High Temperature Glass Ink

High temperature glass ink is composed of dyes, pigments, linkers, additives and other ingredients. As a carrier of pigments, solid particles such as powdered pigments can be mixed and connected, and the adhesive pigments can finally be attached to the surface of the printed matter. It should have good solubility, good pigment dispersion and high substrate adhesion.

2021

12-19

Analyze the development status of screen printing high temperature resistant glass ink

High temperature glass ink is mainly composed of pigments, co-solvents of low melting point glass powder and toner. Among them, pigments are pyrolysis products, and the firing temperature of at least 600 degrees Celsius must be guaranteed. Pigment, as the main material of color development, plays a decisive role in the quality and printability of high temperature glass ink.

2021

12-19

High-temperature glass ink with high audience

High temperature glass ink is also called high temperature tempered glass ink according to the processing temperature. Its sintering temperature is 720-850 ° C. After high temperature tempering, the ink is firmly fused with the glass and is widely used in building curtain walls, automotive glass, stove oven panels, etc.; and the high temperature glass ink baked at high temperature has a sintering temperature of about 500 degrees Celsius and is widely used in glass, ceramics, sports equipment and other industries.

2021

12-19

An important part of high temperature glass ink

Automotive high-temperature glass ink is mainly composed of glass pigments, ink adjustment, additives, etc. Compared with high-temperature glass ink, low-temperature ink is richer and glossier. High-temperature glass ink refers to coating on the inner surface of automotive glass after being treated with a high temperature of 600 to 700 degrees Celsius, which can effectively reduce the UV transmittance, thereby improving in-car comfort and car safety.

2021

12-19

Advantages and disadvantages of high temperature glass ink in the printing process

In order to prevent high-temperature glass ink pollution caused by improper operation during the printing process, the following aspects should be controlled: 1. The positioning of the glass should be accurate when printing.

2021

12-19

The birth of the low-carbon era of high temperature glass ink

It is understood that the third generation of high temperature glass ink has been successfully developed, which means that my country has a higher level in the field of water-based high temperature glass ink.

2021

12-19

< 123 >
图片名称
Message

Glass Decoration

Ceramic Decoration

Functional Material

Learn More

Contact

East China：  Mr.  Peng   +86-18553387033

                       Mr. Zhang   +86-18553397955

North China：Mr. Zhang   +86-13573319588

South China：Mr. Wang   +86-13754763123

Zip code：256401        

E-mail：sales@opalmaterial.com

Add：No. 20, Yihe Road, Guoli Town, Huantai County, Zibo City, Shandong Province

图片名称

Copyright © Zibo Opal Ceramic&Glass Tech Co.,Ltd.

SEO   POWERED BY WWW.300.CN